Optimization for solidification of low-level-radioactive resin using Taguchi analysis

Solidification of low-level-radioactive (LLW) resin was optimized using Taguchi analytical methodology. The ingredients in LLW mortar which caused the solidification of cement were evaluated through consecutive measurements of the effects of various concentrations of ingredients. Samples selected according to Taguchi’s method were separated into 18 different categories and measured at the 7th, 21st, and 28th day after fabrication on developing effects. Evaluations of the various samples focused on whether the compressive and bending strength fulfilled the special criteria of the Taiwan Power Company (TPC). Similar results indicated that both furnace slag and fly ash were the dominant material resulting from the solidification of LLW mortar. The superior combination was obtained as furnace slag 24 wt.%, fly ash 24 wt.%, and cement 8 wt.% to mix 24 wt.% of resin with 20 wt.% of water, to fulfill the contemporary requirements of TPC.