Inertization of pyrite cinders and co-inertization with electric arc furnace flue dusts by pyroconsolidation at solid state

The viability of a pyroconsolidation process to render pyrite cinders inert and to co-inert pyrite cinders with a hazardous polymetallic residue such as electric arc furnace flue dusts (EAF) containing Pb, Cu, Zn, As, Cr, Ni and Mo were investigated. The effects of pyroconsolidation temperature (800–1200 °C), milling pyrite cinders and additions of both CaO and EAF on the resulting microstructure of the pellets were determined. The microstructural changes were then compared with the results of the standard leaching tests. Full inertization of pyrite cinders was achieved after milling to <100 μm followed by a pelletization and pyroconsolidation process at a temperature of 1200 °C. This process also allows co-inertization of pyrite cinders with controlled additions of EAF (up to ≈10%). Following pyroconsolidation at 1200 °C, the metallic elements were inert components in the four main phases: traces of Cr in hematite; Cr, Cu, Zn and Ni in spinel-phase; traces of Cr and Zn in calcium ferrites; and Pb and traces of Cu, Zn and Ba in K–Ca–Al–Fe glassy silicate.