A research program for dynamic fracture evaluation of Japanese carbon steel pipes Original Research Article

A research program was developed to investigate the dynamic load effect on fracture behavior of Japanese carbon steel STS410 pipe. The program comprises material tests, pipe fracture tests and development of estimation scheme. Material property tests showed that the flow stress was nearly constant or slightly increased with strain rate. Pipe tests showed that fracture load was nearly predicted by the net-section collapse criterion for both quasi-static and dynamic loading. Significant dynamic effect was not observed for STS410 carbon steel piping. Crack growth was well formulated by using J-integral parameter for low cycle fatigue with large scale yielding. Combining the crack growth behavior and unstable fracture criterion, an estimation scheme was newly developed and validated for constant amplitude cyclic loading conditions.