Transport properties of long-lengths of RHQT processed Nb/sub 3/Al conductor

A rapid heating and quenching (RHQ) operation along a long-length of jellyroll Nb/Al precursor over 300 m has been established. The J/sub c/ varies sensitively with the joule-heating current (I/sub RHQ/) that determines the temperature from which a precursor wire is quenched, excluding the "plateau" region where the bcc supersaturated-solid solution (Nb(Al)/sub ss/) only forms. The RHQ operation using such a plateau condition can suppress a scatter of J/sub c/ from point to tail of a long-length of wire. The standard deviation of J/sub c/ (4.2 K) at 21 T along a long-length of wire was about 5%, which was less than the variation of J/sub c/ with I/sub RHQ/ in the plateau region (+-7%). The mechanical deformation process needed when incorporating the Cu stabilizer also plays an important role in ensuring uniform heat treatment of the coil that is wound with a long-length of wire and, hence, large heat capacity. Although a temperature ramp-up rate might differ from place to place in the coil, the deformation processing makes such a ramp-up rate insensitive to these critical parameters. The coils using 300.5 m and 254 m lengths of Cu-clad RHQT JR Nb/sub 3/Al conductor generated additional 2.3 T and 3.2 T in bores of 90.2 mm(phi) and 64.6 mm(phi), respectively, indicating that a long-length of RHQT JR Nb/sub 3/Al conductor can be trustworthy for practical coil applications.