Title of article :
Sb adsorption on Si(1 1 1)–In(4 × 1) surface phase
Author/Authors :
B.V. Rao)، نويسنده , , D Gruznev، نويسنده , , T Tambo، نويسنده , , C. Tatsuyama، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2001
Pages :
8
From page :
187
To page :
194
Abstract :
We studied the formation of first InSb molecular layer on the Si(1 1 1) substrate by depositing about 1 ml of Sb on In(4×1) reconstruction in the temperature range 170–350°C, using reflection high-energy electron diffraction (RHEED) and auger electron spectroscopy (AES). The element Sb deposition at 210°C resulted in the formation of an epitaxial InSb molecular layer (not psudomorphic). This surface showed a weak 1×1 RHEED pattern with a ‘dramatic rotation’ of the surface layer with respect to the Si substrate. At this temperature, the deposited Sb atoms do not replace the Si–In bonds. However, Sb deposition above 250°C resulted in the replacement of In-layer by Sb atoms. Subsequently Sb formed various well-ordered reconstructions, which are highly sensitive to the deposition conditions. 1 ml Sb deposition on In(4×1) reconstruction at 260, 300 and 350°C formed 2×1, 2×2 and √3×√3 structures, respectively. All these surface phases produced very sharp RHEED patterns indicating the long-range order. For Sb depositions above 300°C, AES results showed negligible In presence on the Si surface, suggesting the coalescence of In reconstruction by the adsorbed Sb. This replacement reaction drastically changes the bonding nature of the Si surface, which explains the role played by the In(4×1) reconstruction for the InSb growth on Si(1 1 1) substrate.
Keywords :
Si(1 1 1)–In(4×1) reconstruction , Sb adsorption , Interface formation , InSb , Auger electron spectroscopy , Reflection high-energy electron diffraction
Journal title :
Applied Surface Science
Serial Year :
2001
Journal title :
Applied Surface Science
Record number :
997031
Link To Document :
بازگشت