abdulsalam k. s., . ministry of science and technology - directorate of materials science, iraq , maria. g. r., . university of naples federico ii - institute of composite and biomedical materials, c n r, Italy , thair l., . ministry of science and technology - directorate of materials science, iraq , hameed r., . ministry of science and technology - directorate of materials science, iraq , saiyah, murtda a. ministry of science and technology - directorate of chemical and petrochemical industries, Iraq
چكيده فارسي :
starting materials for producing hydroxyapatite (HAP). The product formed wereThe sol-gel route using an agar gel with calcium nitrate and phosphate solution as needle like, zigzag and straight fibres. The fibrous products on sintering transformed into stoichiometric HAP with a biological Ca/P ratio of 1.67 The influences of pH, temperature, nature of base and phosphate solution on the growth of fibrous HAP were studied. The pH of the solution was found to greatly influence the growth rate and morphology of the resultant product. The optimum gel temperature was found to be 60oC and sintering temperature of 900°C for 1 hour. The crystalline, thermal, functional and morphological characteristics of the fibrous HAP were investigated
كليدواژه :
Bioceramic , hydroxyapatite , sol , gel , biocompatibility , agar.