تحضير معدن هيدروكسيصودلايت أحادي الطور من الكاولين واطيء الجودةوتطبيقاته في امتصاص الرصاص

19

30

12

Low grade kaolin is converted to monolith hydroxysodalite dihydrate by hydrothermal treatment with 10M NaOH solution i.e., higher Na concentration, Na/Si =1.3. The X-ray diffraction and infrared methods are used to determine the chemical formula of cured material which is Na8Al6Si6O24(OH)2.2H2O. The CEC values do not correlate with that of SSA values, where for uncured kaolin the CEC have increased from 6.52 to 89.13 meq/100g for the cured kaolin or synthetic hydroxysodalite; on the other hand, the SSA values have decreased from 87 to 10 m2/g. An adsorption experiment shows that the expansion of the framework of hydroxysodalite is due to the replacement of Na+ by Pb2+; moreover, about 91% of Pb is effectively removed. To get optimum removal, the solution must be buffered to about pH=4.5.

تم تحضير معدن احادي الطور من الهيدروكسيصودلايت ثنائي جزيئة الماء من المعالجة الحرمائية لاطيان الكاولين واطئة الجودة مع محلول هيدروكسيد الصوديوم 10 مولاري (بتركيز صوديوم عالي ونسبة صوديوم/سليكون =1.3). استخدمت تقنية الاشعة السينية الحيودية والاشعة تحت الحمراء لتحديد الصيغة الكيميائية للمادة المحضرة والتي هي: Na8Al6Si6(OH)2.2H2O. إن قيم سعة التبادل الكاتيوني لا تتوافق مع قيم المساحة السطحية النوعية, اذ ان سعة التبادل الكاتيوني للمادة غير المعالجة (أطيان الكاولين) ازدادت من 6.52 الى 89.13 ملليمكافىء /100غم للهيدروكسيصودلايت المحضر؛ من جهة اخرى, ان قيم المساحة السطحية النوعية تقل من 87 الى 10 م2/غم, على التوالي. بينت تجارب الامتصاص ان تمدد الشبكة البنائية للهيدروكسيصودلايت هي بموجب احلال ايون الرصاص محل ايون الصوديوم؛ علاوة على ذلك, تم ازالة حوالي 91% من الرصاص الموجود في المحلول. لغرض الحصول على القيم المثلى للازالة, يجب تنظيم درجة حامضية المحلول الى حوالي 4.5.

Hydroxysodalite , Application , Kaolin

2007

المجله العراقيه الوطنيه لعلوم الارض

المجله العراقيه الوطنيه لعلوم الارض