Author/Authors :
Omid Bakhtiari Department of Chemical Engineering, Razi University, Kermanshah, Iran , Samira Mosleh Research Center for Membrane Separation Processes, Department of Chemical Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran , Tayebeh Khosravi Research Center for Membrane Separation Processes, Department of Chemical Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran , Toraj Mohammadi Research Center for Membrane Separation Processes, Department of Chemical Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran
كليدواژه :
Mixed Matrix Membrane , Polyimides , Zeolite 4A , CO2 permeation
چكيده لاتين :
CO2 removal and / or capturing is one of the most important tasks in gas separation and environmental
protection. Some mixed matrix membranes (MMMs) were fabricated in order to improve membrane
separation performance of CO2 selective permeation using polyimide of Matrimid 5218 as backbone
and zeolite 4A as filler. Scanning Electron Microscopy (SEM) analysis showed acceptable
connections between the two phases and the MMMs performed higher performances for CO2
permeation compared with the neat polymeric membrane to some extent. Although a glassy polyimide
was used, thermal treatment at a temperature around glass transition temperature (Tg) of the polyimide
repaired probable defects and there were no voids around the fillers, as gas permeation tests revealed.
Also, MMMs showed higher thermal stabilities than that of neat polymeric membrane. This is
essential for many CO2 separation and capturing operations.