پديدآورندگان :
Javaheri Mohammad Mobin mohammadmobinjavaheri@gmail.com Department of Materials and Textile Engineering, Faculty of Engineering, Razi University, Kermanshah, Iran , Zangeneh Shahab shzangeneh@razi.ac.ir Department of Materials and Textile Engineering, Faculty of Engineering, Razi University, Kermanshah, Iran , Ali Nozari Mohammad mohammadali.nozarii@gmail.com Department of Materials and Textile Engineering, Faculty of Engineering, Razi University, Kermanshah, Iran , Ahmadifard Kimia Department of Materials and Textile Engineering, Faculty of Engineering, Razi University, Kermanshah, Iran , Sharifi Pegah Department of Materials and Textile Engineering, Faculty of Engineering, Razi University, Kermanshah, Iran , Eliasi Rojhin Department of Materials and Textile Engineering, Faculty of Engineering, Razi University, Kermanshah, Iran
كليدواژه :
Cobalt alloy , rolling , carbides , plastic deformation
چكيده فارسي :
In this study, an attempt to investigate strain-induced phase transformation in Co-26Cr-10Ni-8W alloy using up to 50% cold rolling has been made. The primarily as-cast microstructure of Co-26Cr-10Ni-8W alloy consists of M6C and M23C6 carbides while the obtained results showed that M6C carbide was dissociated by the carbon traps in dislocations generated during the plastic deformation.