Effect of dual equal channel lateral extrusion on the shear mechanical properties and corrosion resistance of ZK60 alloy
پديدآورندگان :
Fakhar Naeimeh naemeh.fakhar@gmail.com Mechanical Engineering Department, Hamedan University of Technology, 65155-579 Hamedan, Iran , Sabbaghian Mahdi msabbaghians@ut.ac.ir School of Metallurgical and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
كليدواژه :
ZK60 Mg alloy , DECLE process , Corrosion resistance , Strength
عنوان كنفرانس :
دوازدهمين كنفرانس بين المللي مهندسي مواد و متالورژي
چكيده فارسي :
A hot rolled-annealed ZK60 Mg alloy was deformed by 1 pass dual equal channel lateral extrusion (DECLE) process. The coarse grain structure of 68 μm in the rolled sample was changed to a fine grain structure with a size of 2 μm distributed around coarse grains of 20–80 μm. Shear punch testing results indicated that DECLE increased the strength from 227.6 MPa to 237.3 MPa due to the fine grains and presence of second phase particles at the grain boundaries. However, the bimodal structure and presence of coarse second phase particles after 1 pass DECLE accelerated the galvanic corrosion mechanism and decreased the corrosion resistance.