Effects of nano-cellulose and additives on adhesion strength of acrylic coating used on beech wood
پديدآورندگان :
Akbarnezhad M نويسنده , Rasouli Davood نويسنده Department of Nursing, Urmia University of Medical Sciences, Urmia, IR Iran , Yousefi H نويسنده Assistant professor, Renewable Energies and Environmental Engineering Department, University of Tehran, Tehran, Islamic Republic of Iran , Mashkour M نويسنده
كليدواژه :
adhesion strength , Nanofibrillated cellulose , hydroxyl benzophenone , transparent paints , acrylic
عنوان كنفرانس :
The 6 th International Color & Coating Congress
چكيده فارسي :
the present study, the effects of nanofibrillated cellulose (NFC) with hydroxyl benzophenone , zinc peroxide or nano-zinc oxide were studied on the adhesion strength of transparent acrylic paints covered on beech wood. Parallel specimens with size of (100.0 ± 0.5) mm × (100.0 ± 0.5) mm × (20.0 ± 0.5) mm were preconditioned at a temperature of (23.0 ± 0.2) ◦C and (50 ± 3) % relative humidity prior to testing as recommended by ASTM D 3294. Then all sample surfaces were painted by brush, and strength test were performed. Results revealed that NFC modified by hydroxyl benzophenone had highest bonding strength, whereas the lowest bonding strength was observed in NFC modified by Zinc peroxide.
شماره مدرك كنفرانس :
4184098