subaşi, mehmet gazi university - technical sciences vocational school of higher education, Turkey , safarian, asghar islamic azad university, maragheh branch - young researchers and elite club, ايران , karataş, çetin gazi university - faculty of technology - department of manufacturing engineering, Turkey
Title Of Article
An Investigation of Injection Parameters of Ti-6Al- 7NbFabricated by Powder Injection Molding
شماره ركورد
15935
Abstract
In this study, the optimized injection parameters for a feedstock obtained by mixing the powder of Ti-6Al-7Nb and 31wt% binder system (comprised of high-density polyethylene, Polypropylene, PEG 20000, paraffin wax and stearic acid), were determined. In order to investigate the fabrication of a component, flow rate, injection pressure, holding pressure, injection temperature and mold temperature were studied at three levels to obtain the optimum injection parameters. It was proven that for feedstock comprised of 69wt% Ti-6Al-7Nb powder, the suitable set of injection parameters were as follows: flow rate of 20 cm3/s, injection pressure of 1300 bar, holding pressure of 60%, injection temperature of 140 °C and mold temperature of 60 °C. At the end of the experiments the tensile strength of specimens fabricated with optimum parameters, were as high as 631 MPa.
From Page
393
NaturalLanguageKeyword
Ti , 6Al , 7Nb , Powder Injection Molding , Injection , Sintering
JournalTitle
Journal Of Polytechnic
To Page
399
JournalTitle
Journal Of Polytechnic
Link To Document