GÖKMEŞE, Hakan Gazi Üniversitesi - Metalurji ve Malzeme Mühendisliği Bölümü, Türkiye , BOSTAN, Bülent Gazi Üniversitesi - Metalurji ve Malzeme Mühendisliği Bölümü, Türkiye

MICROSTRUCTURAL CHARACTERIZATION AND SYNTHESIS BY MECHANOCHEMICAL METHOD OF NANO PARTICLE Al2O3/B4C CERAMIC PHASE

16769

In this study, producabilityof Al2O3/B4C ceramic phases at room temperaturecontrary high temperatureproduction methods (carbothermal reduction, sol gel, chemical vapor deposition etc. ) using the ternary system of B2O3-Al-C was investigated as mechanochemical. The starting materials were activated in attritor, planetary and spex ball mill under argon atmosphere at different times. The characterization of ceramic phase powder mixtures synthesized was investigated by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) XRD studies showed that Al2O3/B4C ceramic phases were formed by using spex after 10h of milling. The agglomeration phenomenon with decrease (50-200 nm) in the powder size were determined as a result of mechanical energy and increase in amount ofceramic phaseformed.TEM studies showed that the products after the leaching process were yielded the efficient distributionofthe ceramic phases with the removal of contaminations.

289

Mechanochemical synthesis , nanoparticle , leaching , tem

Journal Of The Faculty Of Engineering an‎d Architecture Of Gazi University

297