Title Of Article
Corrosion Behavior of AA5754 Thin Sheets Welded with Cold Metal Transfer Method
شماره ركورد
29493
Abstract
AA5754 aluminium alloy are widely used in outer and inner panels of automobiles. Present study aimed to investigate the corrosion rate of cold metal transfer (CMT) welded 2 mm thick AA5754 sheets. Welded sheets were produced with 73.97, 86.18, 108.99 J/mm heat input values using ER5356 filler wire. Effect of heat input on corrosion rate was determined by Tafel extrapolation method. It was determined that corrosion rate increased with increasing heat input. Corroded surfaces were viewed by SEM. Hardness test was applied and maximum hardness values were observed in weld metal.
From Page
907
NaturalLanguageKeyword
AA5754 , CMT welding , corrosion
JournalTitle
Journal Of Polytechnic
To Page
911
JournalTitle
Journal Of Polytechnic
Link To Document