özdinçer, mesut duzce university - faculty of technology - department of composite materials, Duzce, Turkey , durmuş, sefa duzce university - faculty of arts and sciences - department of chemistry, Duzce, Turkey , dalmaz, aslıhan duzce university - faculty of arts and sciences - department of chemistry, Duzce, turkey
Title Of Article
Magnetic Spinel-Type CoFe2O4 Nanoparticles: Synthesis and Investigation of Structural, Morphological Properties
شماره ركورد
32892
Abstract
Spinel-type metal oxide nanoparticles were synthesized via co-precipitationapproach. Mono ethylene glycol (MEG) was used as a capping agent to stabilize theparticles and prevent them from agglomeration. The structural, morphological and thermalproperties of the calcined sample were characterized by X-ray diffraction (XRD), scanningelectron microscopy (SEM), raman spectroscopy and thermal analysis. Energy-dispersiveX-ray analysis (EDX) has also proved that the element composition was composed of puresingle phase and contained Co, Fe and O elements. The mean crystallite size of theprepared ferrite nanoparticles was determined to be in the range of 30-345 nm based onthe SEM images. The magnetic measurements of the CoFe2O4 nanoparticles wereexamined with a vibrating sample magnetometer (VSM) at room temperature to determinetheir magnetic behavior and the magnetic parameters were found.
From Page
311
NaturalLanguageKeyword
CoFe2O4 , Ferrite , Nanoparticles , Raman , SEM , Spinel
JournalTitle
Journal Of Natural and Applied Sciences
To Page
315
JournalTitle
Journal Of Natural and Applied Sciences
Link To Document