ayas, erhan anadolu university - department of materials science and engineering, Eskişehir, Turkey

MECHANICAL, ELECTRICAL AND THERMAL PROPERTIES OF α/β SiAlON-SiC COMPOSITES FABRICATED BY GAS PRESSURE SINTERING METHOD

34338

α/β SiAlON-SiC composites were produced by coating SiAlON based spray dried granules with varying amounts of SiC (0-10 vol % SiC) following gas pressure sintering technique. A two step sintering schedule between 1940-1990°C under 10 MPa N2 gas pressure was adopted in order to achieve high densification rate. All the composites and the reference SiAlON material were densified up to 99 %. α/β SiAlON - 10 vol. % SiC composite had the highest hardness value (Hv10: 16.33 GPa) due to the formation of α-SiAlON phases promoted with the increasing SiC content. No significant changes in the fracture toughness values of composites were observed. 3D segregated network of SiC particles along granules to establish electrical and thermal conductivity in the composites was successfully achieved with incorporation of 10 vol. % SiC. α/β SiAlON - 10 vol. % SiC composite exhibited the semiconductor characteristic and high thermal conductivity with the electrical resistivity of 10^2 Ω.m and thermal diffusivity of ~11 mm^2/s measured at room temperature.

812

SiAlON , SiC , Electrical conductivity , Thermal conductivity, Gas pressure sintering (GPS)

Anadolu University Journal of Science and Technology. A : Applied Sciences and Engineering

822