DocumentCode :
1240616
Title :
Influence of porosity on the critical currents of trifluoroacetate-MOD YBa2Cu3O7 films
Author :
Castaño, O. ; Cavallaro, A. ; Palau, A. ; González, J.C. ; Rosell, M. ; Puig, T. ; Piñol, S. ; Mestres, N. ; Sandiumenge, F. ; Pomar, A. ; Obradors, X.
Author_Institution :
Inst. de Ciencia de Mater., CSIC, Barcelona, Spain
Volume :
13
Issue :
2
fYear :
2003
fDate :
6/1/2003 12:00:00 AM
Firstpage :
2504
Lastpage :
2507
Abstract :
The influence of porosity on the superconducting properties have been investigated on YBa2Cu3O7 thin films deposited on LaAlO3 [100] substrates by the so-called Trifluoroacetate (TFA) route. Micro-Raman spectroscopy have been used to determine the concentration of c-axis grains δ in different samples and their influence on the final film porosity as observed from SEM imaging. This has been compared with measurements of resistivity and critical currents in the same samples. We prove that this δ fraction is the main parameter controlling the porosity and hence the normal-state resistivity of the thin films. The optimization of the microstructure of these YBa2Cu3O7 TFA films allow to have high critical currents : Jc = 3 × 106 A/cm2 at 77 K.
Keywords :
MOCVD coatings; Raman spectra; barium compounds; critical current density (superconductivity); electrical resistivity; high-temperature superconductors; porosity; superconducting tapes; superconducting thin films; yttrium compounds; 77 K; LaAlO3; SEM imaging; YBa2Cu3O7; YBa2Cu3O7 films; c-axis grains; critical currents; high critical currents; high temperature superconductor; micro-Raman spectroscopy; microstructure; normal-state resistivity; porosity; resistivity; superconducting properties; trifluoroacetate-MOD; Atmosphere; Conductivity; Critical current; Microstructure; Optical films; Substrates; Superconducting films; Superconducting thin films; Temperature; Yttrium barium copper oxide;
fLanguage :
English
Journal_Title :
Applied Superconductivity, IEEE Transactions on
Publisher :
ieee
ISSN :
1051-8223
Type :
jour
DOI :
10.1109/TASC.2003.811832
Filename :
1212124
Link To Document :
بازگشت