Partial discharge resistant characteristics of epoxy nanocomposites

Epoxy nanocomposite samples with a good dispersion of alumina nanoparticles in epoxy matrix were prepared and experiments were performed to measure their partial discharge resistant characteristics. Epoxy alumina nanocomposites with 0.1, 1, 5, 10 and 15 wt% nanofillers were prepared in the laboratory and partial discharge (PD) experiments were conducted at a voltage of 10 kV for different durations using IEC (b) type electrodes. The degradation of the sample surfaces were analyzed using SEM techniques, surface profile studies, FTIR spectroscopy as well as PD studies. An attempt was made to understand the interaction dynamics between the nanoparticle and the epoxy chain by measuring the glass transition temperature of the nanocomposites. The partial discharge resistance obtained for the nanocomposites are compared with those of unfilled epoxy and epoxy microcomposites. It was observed that even with 0.1 wt% of nanofiller added to the epoxy matrix, the partial discharge resistance to degradation gets improved considerably. It was also observed that the inter particle distance has a significant effect on the discharge resistance to degradation. The improvement in the degradation resistance is attributed to the interactions between the nanoparticle and the epoxy chain. A possible mechanism for the surface degradation of nanocomposites has been proposed.