Title :
Fabrication and properties of high J/sub c/ multifilamentary (Bi,Pb)-2223 tapes with Ag-alloy sheath
Author :
Zhang, P.X. ; Maeda, H. ; Zhou, L. ; Li, C.S. ; Duan, Z.Z. ; Zheng, H.L.
Author_Institution :
Inst. for Mater. Res., Tohoku Univ., Sendai, Japan
fDate :
6/1/1999 12:00:00 AM
Abstract :
(Bi,Pb)-2223 tapes with 37 filaments have been fabricated by powder in tube (PIT) method. Silver was used for the sheath of filaments and the Ag-Mn-Ni alloy was used for the outer sheath of the tapes. A high critical current density of 29000A/cm/sup 2/ (77 K, 0 T) has been achieved in rolled tape with Ag-alloy sheath, in this case the critical current of the tapes is 81.5A, which is higher than that of multifilamentary tapes with pure Ag sheath prepared by the same process. The precursor powders prepared by mixing the (Bi,Pb)-2212 and CaCuO/sub 2/ has been considered to be beneficial for fabricating high J/sub c/ multifilamentary tapes with Ag-alloy sheath. The superconducting properties and microstructural characteristics of the multifilamentary tapes have been investigated in this work.
Keywords :
bismuth compounds; calcium compounds; critical current density (superconductivity); crystal microstructure; high-temperature superconductors; lead compounds; manganese alloys; multifilamentary superconductors; nickel alloys; powder technology; silver alloys; strontium compounds; superconducting tapes; (BiPb)/sub 2/Sr/sub 2/Ca/sub 2/Cu/sub 3/O-AgMnNi; 77 K; 81.5 A; Ag-Mn-Ni alloy; Ag-alloy sheath; CaCuO/sub 2/; PIT method; fabrication; high J/sub c/ multifilamentary (Bi,Pb)-2223 tapes; high J/sub c/ multifilamentary tapes; high critical current density; microstructural characteristics; powder in tube method; precursor powders; rolled tape; superconducting properties; Conductors; Critical current density; Fabrication; Magnetic field induced strain; Performance analysis; Powders; Silver; Stress; Superconducting magnets; Wires;
Journal_Title :
Applied Superconductivity, IEEE Transactions on