Measurement of the dielectric strength of titanium dioxide ceramics

Titanium dioxide ceramics (TiO/sub 2/) are candidate materials for high energy density pulsed power devices. Experiments to quantify the dielectric strength of TiO/sub 2/ have been performed on a limited number of unoptimized samples. A high voltage test set was constructed to test the TiO/sub 2/. All samples had a relative dielectric constant of 100, all samples were of 3 mm nominal thickness, and all tests were performed in water dielectric to reduce the effect of the triple point field enhancement at the electrode edge. Both single layer and laminated samples were tested and the breakdown field strengths were recorded. Voltage risetimes varied slightly around 400 ns depending upon the size of the test sample area. Areas varied from <0.2 cm/sup 2/ to >100 cm/sup 2/. Both single layer and laminated material showed a strong area effect where the dielectric strength dropped off as area to the -0.17 and -0.1 power respectively. Effective areas of the electrodes were calculated using a field solver program. Breakdown field strengths varied from 469 kV/cm to 124 kV/cm in the single layer specimens, and from 556 kV/cm to 261 kV/cm in the laminates over an increasing area range. Energy density calculations for the material show that at areas of approximately 100 cm/sup 2/ the laminates can store nearly 3 times more energy than single layers.