Ultrasonic monitoring of ply crack and delamination formation in composite tube under torsion load

As a simple model of a rotor spar, a circular graphite-epoxy composite laminate cylinder was subjected to cyclic torsional load. The test section of the cylindrical specimen varied from four to six plies of ±45° fibers, due to intentional ply overlaps and gaps. A layer of 13-μm Teflon film was inserted between plies at three locations to serve as delamination initiators. A commercial X-Y scanner was mounted to the load frame to enable ultrasonic inspection without removing the specimen. A focused immersion probe was mounted in a captive water column with a rugged Nitrile membrane tip, which was coupled to the cylinder using a mist of soapy water. The transducer was aligned normal to the cylinder surface using the X-axis. Scanning was performed along the length of the specimen with the Y-axis and the specimen was incrementally rotated by the torsion head of the load frame. After 350k cycles of torsion, several linear 45° diagonal indications appeared as 5-40% attenuation of the back wall echo, with no apparent echoes from the interior of the composite, suggesting through-ply cracks in the innermost ply. Crack indications grew and new cracks appeared as torsion cycling continued. Internal reflections from delaminations associated with the growing ply cracks appeared after 500k cycles. Three areas of extensive multi-layer delaminations appeared after 1150k cycles. Failure of the specimen occurred at 1600k cycles. The observed progressive damage was not associated with the Teflon inclusions. Concurrent thermographic measurements provided lower-resolution confirmation of the damage observed.