High quality AlGaN grown on GaN template with HT-AlN interlayer

When AlGaN is grown on GaN template, crack networks invariably generate when the thickness of the AlGaN layers over GaN exceeds the critical value. We used thin high temperature deposited AlN layer (HT-AlN) as the interlayer between GaN template and AlGaN epilayer which was very effective in eliminating the cracks in AlGaN epilayer. AlGaN layers with high Al mole fractions were also grown. Characterization showed that the crystalline quality of AlGaN epilayer was fairly good even when the Al mole fraction was high.