Luminescent of nano-diamond field emission

Author

Zhang, Xiuxia ; Wei, Shuyi ; Yang, Xiaocong ; Zhang, Lixia ; Wang, Erlei

Author_Institution

Sch. of Mech. Eng., Xi´´an Jiaotong Univ., Xi´´an, China

fYear

2012

fDate

9-13 July 2012

Firstpage

1

Lastpage

2

Abstract

In this paper, the low-cost sol-gel method was adopted to prepare transparent uniform Nano-diamond films on large areas of ITO glass. The mixture of Nano-graphite and organic vehicles doped to nano-diamond paste. After fabricating paste, the Nano-diamond was further ultrasonic dispersed. Through test a variety different content proportion of Nano-diamond paste, the best suitable paste proportion was found. Nano-diamond film was prepared by sol-gel method at 3000/min. The samples of Nano-diamond transparent film were micro-analyzed and tested the field emission characteristics.

Keywords

diamond; field emission; glass; graphite; luminescent devices; nanofabrication; sol-gel processing; thin film devices; ultrasonic dispersion; C; ITO glass; fabricating paste; luminescent; nanodiamond field emission characteristic; nanodiamond paste; nanographite mixture; organic vehicle; sol-gel method; transparent uniform nanodiamond films preparation; ultrasonic dispersion; Cathodes; Current measurement; Educational institutions; Films; Power supplies; Resistance; Voltage measurement; Field emission; Luminescence; Nano-diamond transparent film; sol-gel method;

fLanguage

English

Publisher

ieee

Conference_Titel

Vacuum Nanoelectronics Conference (IVNC), 2012 25th International

Conference_Location

Jeju

ISSN

pending

Print_ISBN

978-1-4673-1983-6

Electronic_ISBN

pending

Type

conf

DOI

10.1109/IVNC.2012.6316891

Filename

6316891