In-situ flexural OPV measurements on flexible glass substrate

In-situ dark and light IV characteristics of inverted P3HT-PCBM devices on flexible glass substrates were measured while bending. Bending set up was simple and home built with servo controlled 2 parallel plate movements. ITO was sputter coated onto the thin flexible glass sheets of 25mm×25mm size in the lab. OPV devices were fabricated inside the glove box and conversion efficiency measured was about 2.8%. Bending of the device substrates and simultaneous PV measurements were carried out in ambient conditions. It was observed that the JSC and efficiency increased until the substrate breaking point but the VOC and fill factor remained unchanged.