Thermal annealing effect on the Mg doped AlGaN/GaN superlattice

Mg-doped AlGaN/GaN superlattice has been grown by metalorganic chemical vapor deposition (MOCVD). Rapid thermal annealing (RTA) treament are carryied out on the samples under nitrogen as protect gas. Hall, photoluminescence (PL) and atomic-force microscopy (AFM) are used to characterize the electrical, optical and structural properties of the as-grown and annealed samples, respectively. After annealing, the Hall results indicate more Mg acceptors are activated, which leads to higher hole concentration and lower p-type resistivity. The PL intensity of Mg related defect band shows a strong decrease after annealing. Many nanometer-grains can be observed on the surface of AlGaN/GaN superlattice from the AFM image. This maybe related with the decomposing of GaN or the separating of Mg from the AlGaN/GaN superlattice.