    Role of Cr3+ on Perpenedicular Magnetic Anisotropy in CoCr Ferrite Thin Films for Magneto-Optic Memory

  • Author

    Yasuhara, T. ; Gomi, M. ; Abe, M.

  • Author_Institution
    Tokyo Inst. of Tech., Faculty of Engng., Tokyo.
  • Volume
    2
  • Issue
    8
  • fYear
    1987
  • Firstpage
    750
  • Lastpage
    751
  • Abstract
    The contribution of Cr3+ substitution to perpendicular magnetic anisotropy in CoCr ferrite film fabricated by varying the Cr3+ substitution amount was studied. As the Cr3+ content increased in the CoCrxFe2-xO4 (x = 0.5, 0.75, 1, 1.25) films, saturation magnetic field decreased and the squareness ratio increased, showing the increase of perpendicular magnetic anisotropy. Films with x greater than 1 had magnetic easy axis perpendicular to the film plane. This result is related to the fact that as Cr3+ substitution amount increased, saturation magnetization decreased from 240 emu/cm3 (x = 0.5) to 24 emu/cm3 (x = 1.25).
  • Keywords
    Chromium; Ferrite films; Magnetic anisotropy; Magnetic films; Magnetooptic effects; Magnetostriction; Perpendicular magnetic anisotropy; Saturation magnetization; Steel; Substrates;
  • fLanguage
    English
  • Journal_Title
    Magnetics in Japan, IEEE Translation Journal on
  • Publisher
    ieee
  • ISSN
    0882-4959
  • Type

    jour

  • DOI
    10.1109/TJMJ.1987.4549598
  • Filename
    4549598
    • Link To Document
    https://search.isc.ac/dl/search/defaultta.aspx?DTC=49&DC=770842