Strong asymmetric stresses arc-induced in pre-annealed nitrogen-doped fibres

Long-period gratings were written using arc discharges in pristine nitrogen doped fibres. Comparison of the resulting gratings spectra show that the resonant positions of gratings in fibres pre-annealed at 1050°C for 30 min are shifted towards shorter wavelengths and their coupling strength is considerably higher. The refractive index and residual stress profiles were measured before and after annealing, as well as the two-dimensional stress profiles inside the grating region. Arc discharges induce periodic and strong asymmetric stresses in the fibre core of the pre-annealed nitrogen doped fibre.