Reliability of AlInAs/GaInAs heterojunction bipolar transistors

The reliability of high-performance AlInAs/GaInAs heterojunction bipolar transistors (HBTs) grown by molecular beam epitaxy (MBE) is discussed. Devices with a base Be doping level of 5×10¹⁹ cm^-3 and a base thickness of approximately 50 nm displayed no sign of Be diffusion under applied bias. Excellent stability in DC current gain, device turn-on voltage, and base-emitter junction characteristics was observed. Accelerated life-test experiments were performed under an applied constant collector current density of 7×10⁴ A/cm² at ambient temperatures of 193, 208, and 328°C. Junction temperature and device thermal resistance were determined experimentally. Degradation of the base-collector junction was used as failure criterion to project a mean time to failure in excess of 10⁷ h at 125°C junction temperature with an associated activation energy of 1.92 eV