چكيده لاتين :
Mn-Te powder is prepared by SPEX milling method. Primary results of air-milled Mn-Te mixture show that original crystallites are gradually broken and oxidized without any MnTe phase formation. X-ray pattern of argon-milled powders show MnTe crystallites after 120 min. milling, accompanying with Mn-Te2 phase. Diffraction peaks of MnTe phase are weakened for longer milling times and some unwanted iron impurity phases gradually appear. The percentage of MnTe phase in products decreases considerably for longer than 12 hours milling times, while MnTe2 phase remains stable even after 110 hours of milling.
عنوان نشريه :
علوم كاربردي و محاسباتي در مكانيك
عنوان نشريه :
علوم كاربردي و محاسباتي در مكانيك
اطلاعات موجودي :
دوفصلنامه با شماره پیاپی سال 1382
كلمات كليدي :
#تست#آزمون###امتحان