اثر ژل هيپوكلريت سديم بر روي استحكام برشي و دوام باند Excite به عاج

Effect of Sodium Hypochlorite gel on shear bond strength and bond durability o f Excite to dentin

Background and Aim: Although bonding mechanism is based on resin diffusion onto the demincralized dentin collagen fibers in most of dentin adhesive systems, it has been shown that the bond is going to degrade over time. The aim of this study was to determine the effect of sodium hypochlorite on shear bond strength and bond durability of Excite to dentin. Materials & Methods: In an experimental study, buccal and lingual surfaces of 36 intact human premolars were prepared and randomly assigned to 4 groups. In groups 1 and 3, specimens were etched and bonding procedures were accomplished according to manufacturerʹs directions. Then, composite resin was bonded to the dentin surfaces. In groups 2 and 4. AD Gel (10% sodium hypochlorite gel) was applied in order to remove the collagen fibers after acid conditioning. Then, the bonding procedure was followed as for groups 1 and 3. After 24 hours, water storage in groups 1 aud 2 and I year water storage in groups 3 and 4, shear bond strength was evaluated and aualyzed by one way analysis of variance. Variance Lest was used for data analysis due to normal distribution of data and homogeneity of variances Results: ANOVA test showed that shear bond strength of group 1 (28.2±7.0 MPa) was significantly higher than group 2 (17.6=i= 8.6 MPa) (P=().()01). The bond strength was also significantly higher in group 3 (29.4±4.7 MPa) than group 4 (2 1.3+ 8.0 MPa) (P^0.009). No statistical significant difference was found between groups 1 and 3 and also between groups 2 and 4 in terms of shear bond strength. Conclusion: Shear bond strength of Excite to dentin decreased with using sodium hypochlorite gel. Shear bond strength of Excite did not show any significant difference after one year of water storage, with or without using sodium hypochlorite gel.