The Effect of Different Bonding Agent Curing Times on Microleakage of Composite Restorations in Enamel and Dentin Margins Using Two Curing Systems

Abstract Background and Aim: Lack of appropriate seal is one of the major problems in composite restorations. Properties of the bonding system can play a crucial role in sealing ability of these restorations. The aim of this study was to evaluate the micro-leakage of class V composite restorations with varying irradiation times for curing dentin bonding agents using two different curing devices. Materials and Methods: In this experimental study, 60 intact extracted human mo-lars and premolars were subjected to standard class V cavity preparations. Cavities were divided to six groups. Following etching, Excite bonding agent was applied and light cured using QTH and LED systems for 20, 30 and 40 seconds and cavities were filled with composite. The filled cavities were subjected to 3000 thermal cycles with 5-55 ° C temperatures. Teeth were immersed in 0.5% basic fuchsine dye and sec-tioned occlusogingivally from the restoration middle area and the microleakage was determined using stereomicroscope by a 5-scaled ranking. Data were analyzed by Mann-Whitney and Kruskal-Wallis tests with p < 0.05 as the level of significance. Results: No leakage was found in enamel margins. The type of light curing device did not have any significant effect on dentin margin microleakage (p > 0.05). Further-more, no significant differences in microleakage scores were observed in the restora-tions irradiated with different curing times (p > 0.05). Conclusion: QTH and LED curing units in 20, 30, and 40 s curing time did not have any significant effect on microleakage of class V composite restoration margins. Key Words: Microleakage, light curing, bonding, polymerization