Author/Authors :
D.S. Galeano-Osorio، نويسنده , , S. Vargas، نويسنده , , L.M. L?pez-C?rdoba، نويسنده , , R. Ospina، نويسنده , , E. Restrepo-Parra، نويسنده , , P.J. Arango، نويسنده ,
Abstract :
Carbon nitride thin films were obtained through plasma assisted physical vapor deposition technique by pulsed arc, varying the substrate temperature and investigating the influence of this parameter on the films hemocompatibility. For obtaining approaches of blood compatibility, environmental scanning electron microscopy (ESEM) was used in order to study the platelets adherence and their morphology. Moreover, the elemental chemical composition was determined by using energy dispersive spectroscopy (EDS), finding C, N and O. The coatings hemocompatibility was evaluated by in vitro thrombogenicity test, whose results were correlated with the microstructure and roughness of the films obtained.
During the films growth process, the substrate temperature was varied, obtaining coatings under different temperatures, room temperature (Troom), 100 °C, 150 °C and 200 °C. Parameters as interelectrodic distance, voltage, work pressure and number of discharges, were remained constant. By EDS, carbon and nitrogen were found in the films.
Visible Raman spectroscopy was used, and it revealed an amorphous lattice, with graphitic process as the substrate temperature was increased. However, at a critical temperature of 150 °C, this tendency was broken, and the film became more amorphous. This film showed the lowest roughness, 2 ± 1 nm. This last characteristic favored the films hemocompatibility. Also, it was demonstrated that the blood compatibility of carbon nitride films obtained were affected by the ID/IG or sp3/sp2 ratio and not by the absolute sp3 or sp2 concentration.
Keywords :
Substrate temperature , Roughness , Carbon nitride films , Hemocompatibility , Raman spectroscopy