Effect of stress peening on surface layer characteristics of (TiB + TiC)/Ti–6Al–4V composite

Residual stresses and microstructure on surface layer of (TiB + TiC)/Ti–6Al–4V are investigated after stress peening. The values of domain sizes and microstrain of surface deformation layers are calculated from the integral breadth of diffractive peaks via Voigt method. The results show that the compressive residual stresses and microhardness are improved significantly after stress peening, and the variations of residual stresses are affected by both the prestresses and the directions of measurement. Microstructure investigations reveal that, the deformation amount increase after stress peening, and smaller domain grain sizes and higher density dislocations are introduced. The changes of microstructures are mainly influenced by the values of prestresses. According to these investigations, it is can be found that the stress peening is superior to the conventional shot peening treatments and it is an effective method to improve the surface properties of (TiB + TiC)/Ti–6Al–4V composite.