A comparative study on thermomechanical and low cycle fatigue failures of a single crystal nickel-based superalloy

The cyclic deformation and lifetime behaviors of a single crystal nickel-based superalloy CMSX-4 have been investigated under out-of-phase thermomechanical fatigue (OP TMF) and isothermal low cycle fatigue (LCF) conditions. OP TMF life exhibited less than a half of LCF life although smaller inelastic strain range and lower mean stress level during OP TMF were observed compared to those during LCF. During OP TMF cycling, the maximum tensile strain at the minimum temperature was found to accelerate the surface crack initiation and propagation. Additionally, the multiple groups of parallel twin plates near crack provided a preferential path for crack propagation.