Abstract :
The phase transition of chromium substituted lithium manganese spinel oxide, LiCryMn2−yO4 was investigated by low-temperature powder X-ray diffractometry (XRD), differential scanning calorimetry (DSC), and electrical resistivity measurements. The sample prepared at 820 °C resulted in lowering the transition temperature Tt with Cr composition y, whereas Tt of the sample prepared at 750 °C remained constant for 0≤y≤0.17 in LiCryMn2−yO4. This would be caused by a difference in distribution of the substituted Cr3+ ion in octahedral site depending on the preparation temperature. The phase transition was suppressed with increasing the amount of Cr content.