Title of article :
Synthesis and microstructure of the Ti3SiC2 in SiC matrix grown by chemical vapor deposition
Author/Authors :
Tien-Chai Lin، نويسنده , , Min Hsiung Hon، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2008
Abstract :
Ti3SiC2 + SiC and TiC + SiC were deposited on graphite substrate at 1300–1600 °C by chemical vapor deposition with TiCl4, SiCl4, C3H8, H2 as reactive gases. Process parameters such as temperature, pressure, concentration of C3H8 were varied to study their effects on the phases and microstructure of the deposited layers. The results show that binary phases of Ti3SiC2 + SiC are formed at temperature less than 1400 °C. For temperature above 1500 °C, TiC + SiC phases are formed. Increase of the process pressure causes the disappearance of Ti3SiC2 and the formation of TiC. The surface morphology of Ti3SiC2 shows a plate-like structure. The hardness of Ti3SiC2 + SiC and TiC + SiC is HV4251 and HV4612 respectively for a load of 10 g.
Keywords :
chemical vapor deposition , B. Composites , C. Hardness , D. Carbides
Journal title :
Ceramics International
Journal title :
Ceramics International