EXAFS, X-ray diffraction and Raman studies of (Pb1−xLax)(Zr0.65Ti0.35)O3 (image and 0.09) ceramics irradiated by high-current pulsed electron beam Original Research Article

We report the effect of pulsed electron beam irradiation on the long-range and short-range atomic structure, as well as on the Raman phonon modes, of perovskite (Pb1−x Lax )(Zr0.65Ti0.35)O3, x=0.04x=0.04 and 0.09 (PLZT 4/65/35 and 9/65/35) ferroelectric ceramics. X-ray powder diffraction (XRD) spectra from the single-pulse-irradiated PLZT 9/65/35 samples reveal transformation of the cubic Pm3m (Z=1Z=1) into the orthorhombic Pmmm (Z=1Z=1) structure. This symmetry change is however not observed for 10-pulse irradiation performed under the same conditions: here only an increase in the coherent scattering regions, lattice volume, and the Zr–O distance distribution is observed, as revealed by XRD and X-ray absorption spectroscopy at Zr K-edge. Raman scattering from PLZT 9/65/35 ceramics is in agreement with the symmetry reduction after single-pulse irradiation and reveals significant Raman signal intensity decrease after multiple-pulse irradiation. On the contrary, no significant structural changes could be detected in PLZT 4/65/35 ceramics after single- or multiple-pulse irradiation. Possible mechanisms of pulsed electron irradiation effects in PLZT 4/65/35 and 9/65/35 ceramics are discussed.