Author/Authors :
Dullweber، نويسنده , , T. and Kranz، نويسنده , , C. and Beier، نويسنده , , B. and Veith، نويسنده , , B. and Schmidt، نويسنده , , J. and Roos، نويسنده , , B.F.P. and Hohn، نويسنده , , O. and Dippell، نويسنده , , T. and Brendel، نويسنده , , R.، نويسنده ,
Abstract :
Passivated emitter and rear cells (PERC) are considered to be the next generation of industrial-type screen-printed silicon solar cells. Deposition methods for rear passivation layers have to meet both the high-throughput and low-cost requirements of the PV industry in combination with high-quality surface passivation properties. In this paper, we evaluate and optimise a novel deposition technique for AlOx passivation layers by applying an inductively coupled plasma (ICP) plasma-enhanced chemical vapour deposition (PECVD) process. The ICP AlOx deposition process enables high deposition rates up to 5 nm/s as well as excellent surface recombination velocities below 10 cm/s after firing. A fixed negative charge of −4×1012 cm−2 is measured for ICP AlOx single layers with an interface state density of 11.0×1011 eV−1 cm−2 at midgap position. When applied to PERC solar cells the ICP AlOx layer is capped with a PECVD SiNy layer. We achieve independently confirmed conversion efficiencies of up to 20.1% for large-area (15.6×15.6 cm2) PERC solar cells with screen-printed metal contacts and ICP AlOx/SiNy rear side passivation on standard boron-doped Czochralski-grown silicon wafers. The internal quantum efficiency reveals an effective rear surface recombination velocity Srear of (90±30) cm/s and an internal rear reflectance Rb of (91±1)% which demonstrates the excellent rear surface passivation of the ICP AlOx/SiNy layer stack.
Keywords :
screen printing , Silicon solar cells , Rear passivation , Inductively coupled plasma , Aluminium oxide , AlOx