Abstract :
The dependence of structural properties and surface morphology of Cu–In alloy layers on the composition and sputtering deposition sequence were investigated by X-ray diffraction, scanning electron microscopy and energy-dispersive X-ray spectroscopy. The properties of the co-sputtered alloy layers changed abruptly around the composition boundary when the Cu/In ratio reached 1/2. This can be explained by the effective heat of formation (EHF) model, which has been used to predict the sequence of phase formation for metal diffusion couples. The use of a co-sputtered alloy layer with a high In concentration was not suitable for fabricating solar cells, because the film had a very rough morphology due to large In islands formed on the CuIn2 phase. However, it was possible to minimize this phase by In sputtering followed by co-sputtering with a Cu/In ratio of 1 (Cu–In/In/Glass). This permitted the fabrication of a homogeneous Cu–In alloy layer, which was not possible through the simple co-sputtering.