Abstract :
B4C ultrafine powders were successfully synthesized at 450 °C through a new co-reduction route. The synthesis was carried out in an autoclave by using BBr3 and CCl4 as the reactants and metallic Na as the co-reductant. The X-ray powder diffraction pattern and Raman spectra indicate the formation of B4C. An atomic ratio of B to C of 4.09:1.0 was determined from X-ray photoelectron spectra. Transmission electron microscopy images shows that typical B4C crystallites are composed of uniform ultrafine spherical and rod-like particles.
