Abstract :
PLZT12/40/60 ceramics doped with different Mn content were prepared by a conventional mixed oxide method. The shrinkage of some local crystal cells was confirmed by XRD diffraction. The effect of Mn doping on the hysteresis loop was investigated. A peculiar double-hysteresis-like loop was found and various possible mechanisms were discussed. Random local strains caused by shrunk crystal cells can satisfactorily explain the double hysteresis characteristics. The dependence of the double-hysteresis-like loops on temperature was also investigated. Due to the heat activation of polar moments in shrunk crystal cells, the double-hysteresis-like loops can transform into a normal one when the temperature is rising.