Abstract :
Thin iron films have been grown on (001) GaAs substrates by low pressure metal organic chemical vapor deposition (LP-MOCVD) at different temperatures with the pressure of 150 Torr. X-ray diffraction (XRD) analysis showed that all films have only one strong diffraction peak (110). The surface of Fe film became smooth with increasing the growth temperature. Magnetization measurements showed that the Fe films grown at different temperatures were ferromagnetic with easy axis parallel to the film surface and hard axis perpendicular to the substrates. The field dependence of magnetization along two axes showed a remarkable difference, implying that the samples have strong magnetic anisotropy. Furthermore, when the applied magnetic field is perpendicular to the Fe surface, a sharp jump in the hysteresis loop could be observed, followed by a broad shoulder, which is related to the interface effect, the existence of carbon and the formation of 180∘/90∘ magnetic domains.