Erosion wear of boron carbide ceramic nozzles by abrasive air-jets
Author/Authors :
Jianxin، نويسنده , , Deng، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2005
Pages :
7
From page :
227
To page :
233
Abstract :
Boron carbide nozzles were produced by hot pressing. The erosion wear of this nozzle caused by abrasive particle impact was investigated by abrasive air-jets. Silica, silicon carbide and alumina powders with different hardness were used as the erodent abrasive particles. Results showed that the hardness of the erodent particles played an important role with respect to the erosion wear of the boron carbide nozzles. As the hardness of the erodent particles increases, there is a dramatic increase in erosion rate of the nozzles. The nozzle entrance area suffered from severe abrasive impact under large impact angles, and generated maximum tensile stresses. The wear mechanisms of boron carbide nozzle at this area appeared to be entirely brittle in nature with the evidence of large scale-chipping, and exhibited a brittle fracture induced removal process. While at the nozzle center wall section, most of the particles traveled parallel to the nozzle wall, and showed minimum tensile stresses. The wear mode in this area of the nozzle changed from impact to sliding erosion, and the wear mechanisms appeared to be the lateral cracking owing to a surface fatigue fracture mechanism.
Keywords :
Boron Carbide , Erosion wear , Abrasive air-jet machining , Ceramic nozzles
Journal title :
MATERIALS SCIENCE & ENGINEERING: A
Serial Year :
2005
Journal title :
MATERIALS SCIENCE & ENGINEERING: A
Record number :
2148984
Link To Document :
بازگشت