The dynamic recrystallization of the Ni-base alloy Bِhler L306 VMR (Alloy 80A) in a transient state was investigated both by light microscopy and electron backscatter diffraction (EBSD), and the experimental results were compared with those from simulations. Subgrain structures of the size of the recrystallized grains were observed close to the grain boundaries of the original grains. With increasing strain a texture developed in the deformed fraction. Strong twinning was found in the recrystallized fraction, with area fractions of the twinned grains of around 80% for higher strains. Thus the measured grain sizes strongly depend on the handling of the twins. A pronounced increase in the average grain size of the recrystallized fraction with increasing strain (time) was only observed after twin removal. There was generally good agreement between the measured and the simulated results.