Deposition of Co–Ti alloy on mild steel substrate using laser cladding

Laser cladding of a Co–Ti alloy on a mild steel substrate is studied. Premixed powders with the composition of 85 wt% cobalt and 15 wt% titanium are pre-placed on the substrate and a moving laser beam at different velocities is used to produce clad layers well bounded to the substrate. Characteristics of the clad are investigated using optical microscopy, X-ray diffraction (XRD), energy dispersive spectroscopy (EDS) and microhardness tests. The results reveal that the intermetallic phase TiCo3 and β (i.e. fcc) cobalt are formed in the clad layer. The clad layer can also have major dilution from the substrate depending on the laser scanning velocity. It is observed that a finer microstructure is achievable with higher laser velocities whereas higher hardness is achieved using lower velocities. The latter is due to the formation of a larger fraction of TiCo3 phase.