Erosion and Erosion-Corrosion Behaviors of Sanicro28 Stainless Steel in 3.5% NaCl Environment
پديدآورندگان :
Shahali H. School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran , Ghasemi H.M hghasemi@ut.ac.ir School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran; , Abedini M Department of Metallurgy and Materials Engineering, Faculty of Engineering, University of Kashan, Kashan, Iran.
كليدواژه :
Synergism effect , Erosion , corrosion , Sanicro28 austenitic stainless steel
عنوان كنفرانس :
ششمين كنفرانس بين المللي مهندسي مواد و متالوژي و يازدهمين همايش ملي مشترك انجمن مهندسي متالوژي و مواد ايران و انجمن علمي ريخته گري ايران
چكيده فارسي :
Erosion-corrosion behavior of Sanicro28 stainless steel was investigated. Erosion-corrosion tests were performed using slurry impingement rig in a 3.5 wt.% NaCl solution containing 30 g/l of SiO2 erosive particles with the average size of 315 µm, at four different velocities of 4, 6, 7.5 and 9 m/s under impingement angles 40 and 90º. The pure erosion tests were also carried out in similar conditions by cathodic protection. The corrosion behavior of the samples in the stagnant condition was studied using electrochemical polarization method. Synergistic effect between erosion and corrosion was calculated. The erosion and erosion-corrosion surfaces were studied using scanning electron microscope (SEM). The results showed lower erosion, erosion-corrosion and synergy rates at impingement angle of 90º as compared with 40º. The evaluation of the mass loss due to erosion-corrosion showed a critical velocity of 6 m/s for Sancrio28 austenitic stainless steel. Positive synergism was obtained under all velocities and impingement angles indicating that cathodic protection could decrease the material loss in erosion-corrosion