رسانش جهشي پلارون كوچك در توده هاي آمورف TeO2-V2O5-MoO3

Small Polaron Hopping Conduction in Amorphous TeO2-V2O5-MoO3 Bulk Samples

در كار حاضر، رسانش الكتريكي dc شيشه ها در سيستم (40)TeO2-(60-x)V2O5- (x)MoO3 در گستره دمايي 403-180 درجه كلوين بررسي شده است . از رابطـه رسانندگي - دما، كارايي مكانيسم جهشي پلارون كوچك در دماهاي بالاتر از دماي دبي (T〉ΘD /2 كه T دماي مطلق و ΘD دماي دبي مي باشد) استنباط مي شود .

The DC electrical conductivity of glasses in the (40)TeO2-(60-x)V2O5- (x)MoO3 system has been studied at temperatures between 180 and403 K. From the conductivity- temperature relation, it was found that small polaron hopping (SPH) mechanism was applicable at the high temperatures ( / 2 D T〉Θ ; D Θ and T are Debye temperature and absolute temperature, respectively).