Turku, Nursen Süleyman Demirel Üniversitesi - Fen-Edebiyat Fakültesi - Fizik Bölümü, Turkey , Doğan, Şule Süleyman Demirel Üniversitesi - Fen-Edebiyat Fakültesi - Fizik Bölümü, Turkey , Uçar, Nazım Süleyman Demirel Üniversites - Fen-Edebiyat Fakültesi - Fizik Bölümü, Turkey , Çalık, Adnan Süleyman Demirel Üniversitesi - Teknoloji Fakültesi - Makine Bölümü, Turkey
Title Of Article
The Effect of Boriding Time on Hardness Values of Low Carbon Micro Alloyed Steels
شماره ركورد
36014
Abstract
In this study, hardness values of borided low carbon microalloyed steels were measured. The boronizing treatment was performed at 1123 K under various exposure times using Ekabor-II commercial powders. The presence of FeB and Fe_2B phases in the boride layer of the boronized low carbon microalloyed steels were observed using an X-ray diffractometer and energy dispersive spectroscopy (EDS) analysis. It was concluded that boride layer thickness and hardness values increase with increasing boriding time due to hard boride phases and diffusion as a result of boronizing process.
From Page
147
NaturalLanguageKeyword
Ecabor , XRD , EDX , diffusion , FeB , Fe2B
JournalTitle
Süleyman Demirel University Faculty of Arts and Science Journal of Science
To Page
151
JournalTitle
Süleyman Demirel University Faculty of Arts and Science Journal of Science
Link To Document