Boronizing of 50Fe-50Co alloy and its characterization
شماره ركورد
41016
Abstract
In this study, equiatomic Fe and Co binary alloy was prepared under argon/vacuum atmosphere. 50Fe-50Co alloy was coated with pack boronizing method for the duration of 6 h at 800 °C, 900 °C and 1000 °C. XRD, OM, SEM, SEM-EDS, Vickers hardness measurement devices were applied to characterize, hardness, microstructure, chemical and phase constituents of the synthetized boride layer on Fe-Co alloy. Perfect adhesion of coating to substrate and formation of saw tooth shaped boride layer on the substrate were observed. The coating was composed of Fe_2B and Co_2B phases. The existence and homogenous distribution of Co in the coating was determined. The coating thickness increased with boriding process temperature. The coating hardness did not vary significantly throughout the thickness of the main boride layer.
From Page
1000
NaturalLanguageKeyword
50Fe , 50Co alloy , Pack boriding , Iron boride , Cobalt boride , Tool steels
JournalTitle
Pamukkale University Journal Of Engineering Sciences
To Page
1003
JournalTitle
Pamukkale University Journal Of Engineering Sciences
Link To Document