Fracture analysis for brake drum of the truck
Author :
Ga O-lu ; Wang Wen-yan ; Xie Jing-pei
Author_Institution :
Coll. of Mater. Sci. & Eng., Henan Univ. of Sci. & Technol., Luoyang, China
fYear :
2011
fDate :
15-17 July 2011
Firstpage :
310
Lastpage :
313
Abstract :
By the fracture analysis on HT250 brake drum, we think that the failure of brake drum in use process is due to internal slag in the bottom of brake drum in the casting process, Or because of brake drum in use process produce hot fatigue crack, which instability expansion leed to the fracture.
Keywords :
automotive components; brakes; casting; failure analysis; fatigue cracks; fracture mechanics; slag; thermal stress cracking; HT250 brake drum; brake drum failure; casting process; fracture analysis; hot fatigue crack; instability expansion; internal slag; truck; use process; Fatigue; Iron; Slag; Stress; Surface cracks; Thermal stresses; brake drum; fracture; slag; thermal fatigue;
fLanguage :
English
Publisher :
ieee
Conference_Titel :
Mechanic Automation and Control Engineering (MACE), 2011 Second International Conference on
Conference_Location :
Hohhot
Print_ISBN :
978-1-4244-9436-1
Type :
conf
DOI :
10.1109/MACE.2011.5986920
Filename :
5986920
Link To Document :
بازگشت